Laminated Composite Filter Media is compounded by ultrasonic melting and hot-melt fibre adhesive technology to bond different layers of material together. To enhance physical or chemical performance of filtration media which can be widely used in pleat filter.
Product Performance
1.Flat appearance and high intensity;
2.High stiffness, be easy to pleated;
3.At the condition of reaching the same efficiency, the resistance of the material decrease by 20%;
4.Own the advantage of great dust capacity and extending the life-span of filter.
Product Technical Data
Type | Basic (W.G/㎡) | Thickness (mm) | Strength ①②(Stiffness mg) | 0.3μm@85L/min∙d㎡ | Application | Remarks | |
Resistance(Pa) | Efficiency(%) | ||||||
FC-45 | 115 | 0.85 | 1000 | 8 | 60% | F5 | PP and PET ultrasonic melting |
FC-65 | 120 | 0.88 | 1200 | 18 | 68% | F6 | |
FC-85 | 130 | 0.91 | 1500 | 21 | 80% | F7 | |
FC-95 | 140 | 0.93 | 1800 | 35 | 85% | F8 | |
FC-98 | 145 | 0.95 | 1800 | 40 | 90% | F9-Y10 | |
Note①: Gurley Stiffness are measured per CRAA433(equivalent to EST-RP-CC021.2).
Note②: The listed data for stiffness are taken from standard grade media by Ruizhi. Stiffness can be easily adjusted to meet customers’ requirements.